牌号简介 About
依凡坦24-03是由乙烯和醋酸乙烯经高压自由基聚合而成的无规共聚物。Evatane 24-03的醋酸乙烯含量高,具有柔软性、柔韧性和极性。Evatane 24-03与大多数填料具有很高的粘合强度,可用于生产母粒或HFFR化合物,并可作为沥青改性添加剂。Evatane 24-03也适用于薄膜(铸造或吹塑)挤出,对PE、PS和聚酯具有良好的粘附性。 EVATANE? 24-03 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process. The high Vinyl Acetate content of EVATANE? 24-03 brings softness, flexibility and polarity. EVATANE? 24-03 delivers high cohesive strength with most fillers and can be used to produce masterbatches or HFFR compounds, and can be used as an additive for bitumen modification. EVATANE? 24-03 is also suitable for film (cast or blown) extrusion, and exhibits good adhesion onto PE, PS and polyesters.

产品描述 Product Description
厂家:法国阿科玛 Arkema 类别:EVA EVA 用途:母料;沥青改性;流延薄膜;吹膜; 加工条件:浇铸 casting 性能特点: 柔软性好; 粘结性好; 无规共聚物; 韧性好; Good flexibility,Good bond,Random copolymer,Soft
技术参数 Technical Data
物理性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
熔体质量流动速率 熔融流动指数
190℃, 190℃ / g/10min ASTM D1238
热性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
熔融温度 Melting Temperature 80 ℃ ASTM D4591
维卡软化温度 Vicat Softening Temperature
46 ℃ ASTM D1525
机械性能 额定值 Nominal Value 单位 Units 测试方法 Test Method
邵氏硬度 邵氏A
邵氏 A 83 ASTM D2240
拉伸强度 拉伸强度
23℃ 23°C 27 MPa ASTM D638
拉伸应变 Tensile Elongation at Break
断裂,23℃ 23°C 750 % ASTM D638
备注
1 一般属性:这些不能被视为规格。
2 压 力1 (10N)
3 NF EN 1238