12cr1movg锅炉管是在碳素结构钢的基础上,适当加入一种或数种合金元素,用来提高钢的力学性能、韧性和淬透性。 用此类钢制造的产品,通常需经热处理(正火或调质);其制成的零、部件在使用前,通常需经过调质或表面化学处理(渗碳、氮化等)、表面淬火或高频淬火等处理。因此,根据化学成分(主要是含碳量)、热处理工艺和用途的不同,此类钢大致又可分为渗碳、调质和氮化钢三种。
标准 | 牌号 | 化学成分(%) | ||||||||||||||
C | Si | Mn | P | S | Cr | Mo | Cu | Ni | V | Al | W | Ti | Nb | N | ||
GB3087 | 10 | 0.07~0.13 | 0.17~0.37 | 0.38~0.65 | ≤0.030 | ≤0.030 | 0.3~0.65 | / | ≤0.25 | ≤0.30 | / | / | ||||
20 | 0.17~0.23 | 0.17~0.37 | 0.38~0.65 | ≤0.030 | ≤0.030 | 0.3~0.65 | / | ≤0.25 | ≤0.30 | / | / | |||||
GB5310 | 20G | 0.17~0.24 | 0.17~0.37 | 0.35~0.65 | ≤0.030 | ≤0.030 | ≤0.25 | ≤0.15 | ≤0.20 | ≤0.25 | ≤0.08 | |||||
20MnG | 0.17~0.24 | 0.17~0.37 | 0.70~1.00 | ≤0.030 | ≤0.030 | ≤0.25 | ≤0.15 | ≤0.20 | ≤0.25 | ≤0.08 | ||||||
25MnG | 0.18~0.24 | 0.17~0.37 | 0.80~1.10 | ≤0.030 | ≤0.030 | ≤0.25 | ≤0.15 | ≤0.20 | ≤0.25 | ≤0.08 | ||||||
15CrMo | 0.12~0.18 | 0.17~0.37 | 0.40~0.70 | ≤0.030 | ≤0.030 | 0.80~1.10 | 0.40~0.55 | ≤0.20 | ≤0.30 | |||||||
12Cr2MoG | 0.08~0.15 | ≤0.50 | 0.40~0.70 | ≤0.030 | ≤0.030 | 2.00~2.50 | 0.90~1.20 | ≤0.20 | ≤0.30 | |||||||
12Cr1MoV | 0.08~0.15 | 0.17~0.37 | 0.40~0.70 | ≤0.030 | ≤0.030 | 0.90~1.20 | 0.25~0.35 | ≤0.20 | ≤0.30 | 0.15~0.30 |
所有评论仅代表网友意见,与本站立场无关。