合号 | Cu | Pb | Sn | Zn | P | Cu+Sn+P | ||
C5111 | 3.5~4.5 | 0.03~0.35 | 99.5min | |||||
C5102 | 4.5~5.5 | 0.03~0.35 | 99.5min | |||||
C5191 | 5.5~7.0 | 0.03~0.35 | 99.5min | |||||
C5212 | 7.0~9.0 | 0.03~0.35 | 99.5min | |||||
C5341 | 0.8~1.5 | 3.5~3.8 | 0.03~0.35 | 99.5min | ||||
C5441 | 3.5~4.5 | 3.4~4.5 | 1.5~4.5 | 0.01~0.5 | 99.5min | |||
Cu | Sn | Al | Zn | Ni | Fe | Pb | P | |
QSn6.5-0.1 | 余量 | 6.0~7.0 | 0.002 | 0.3 | 0.2 | 0.05 | 0.02 | 0.10~0.25 |
QSn4-3 | 余量 | 3.5~4.5 | 0.002 | 2.7~3.3 | 0.2 | 0.05 | 0.02 | 0.03 |
机械及物理性能 | ||||||||
Mechanicai properities | ||||||||
状态 | 拉伸试验 | 硬度试验 | 弯曲试验 | |||||
厚度 | 拉伸强度 σb(MPa) | 伸长率 δ10(%) | 厚度 mm | 维氏硬度 HV | 厚度 mm | 弯曲角度 | 弯曲半径 | |
O | 0.15-1.2 | ≥315 | ≥42 | — | — | ≤1.6 | 180°或w | 厚度×0.5 |
1/4H | 390-510 | ≥35 | ≥0.15 | 100-160 | ≤1.6 | 180°或w | 厚度×1 | |
1/2H | 490-610 | ≥20 | ≥0.15 | 150-205 | ≤1.6 | 180°或w | 厚度×1.5 | |
H | 590-685 | ≥8 | ≥0.15 | 180-230 | ≤1.6 | 180°或w | 厚度×2 | |
EH | ≥635 | ≥5 | ≥0.15 | ≥200 | — | — | — | |
合金主要制作弹性元件特别是电导性好的弹簧接触片,仪器仪表中的耐磨零件和抗磁元件等 | ||||||||
合金主要用于造纸、化工和食品等工业制造金属网,也用于制造耐磨和弹簧零件 | ||||||||
合金用于在中等的载荷和滑动速度下承受摩擦的零件,如轴承、轴套、涡轮等,亦可制造弹性元件和其他机械电气零件 | ||||||||
合金用于生产压力表中的各种管材,作敏感元件,有压力表青铜之称 |